| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | plutao.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 8JMKD3MGP3W/44SJQFH |
| Repositório | sid.inpe.br/plutao/2021/06.16.16.11.48 (acesso restrito) |
| Última Atualização | 2021:06.16.18.13.58 (UTC) administrator |
| Repositório de Metadados | sid.inpe.br/plutao/2021/06.16.16.11.49 |
| Última Atualização dos Metadados | 2022:04.03.23.14.14 (UTC) administrator |
| DOI | 10.1590/s1517-707620210002.1267 |
| ISSN | 1579-2641 |
| Rótulo | lattes: 9764742132401600 7 BispoLFPMYABM:2021:12GH |
| Chave de Citação | BispoLFPMYABM:2021:12GH |
| Título | Electromagnetic properties of Carbon-Graphene Xerogel, Graphite and Ni-Zn Ferrite composites in polystyrene matrix in the X-Band (8.2 - 12.4 GHz)  |
| Ano | 2021 |
| Data de Acesso | 04 maio 2024 |
| Tipo de Trabalho | journal article |
| Tipo Secundário | PRE PN |
| Número de Arquivos | 1 |
| Tamanho | 649 KiB |
| 2. Contextualização | |
| Autor | 1 Bispo, Matheus Carvalho 2 Lopes, Braulio Haruo Kondo 3 Fonseca, Beatriz Carvalho da Silva 4 Portes, Roberto Camargo 5 Matsushima, Jorge Tadao 6 Yassuda, Míriam Kasumi Hwang 7 Amaral Labat, Gisele Aparecida 8 Baldan, Maurício Ribeiro 9 Migliano, Antonio Carlos da Cunha |
| Identificador de Curriculo | 1 2 3 4 5 6 7 8 8JMKD3MGP5W/3C9JHTA |
| Grupo | 1 2 COPDT-CGIP-INPE-MCTI-GOV-BR 3 CMS-ETES-DIPGR-INPE-MCTI-GOV-BR 4 5 6 7 COPDT-CGIP-INPE-MCTI-GOV-BR 8 COPDT-CGIP-INPE-MCTI-GOV-BR |
| Afiliação | 1 Instituto Federal de Educação, Ciência e Tecnologia de São Paulo (IFSP) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Instituto Nacional de Pesquisas Espaciais (INPE) 4 Instituto Tecnológico de Aeronáutica (ITA) 5 Faculdade de Tecnologia de São José dos Campos (FATEC) 6 Instituto de Estudos Avançados (IEAv) 7 Instituto Nacional de Pesquisas Espaciais (INPE) 8 Instituto Nacional de Pesquisas Espaciais (INPE) 9 Instituto de Estudos Avançados (IEAv) |
| Endereço de e-Mail do Autor | 1 matheus.bispo@aluno.ifsp.edu.br 2 brauliohkl@gmail.com 3 beatrizalpinopolis@gmail.com 4 robertocportes@gmail.com 5 jtmatsushima@yahoo.com.br 6 miriam@ieav.cta.br 7 gisele.amarallabat@gmail.com 8 mauricio.baldan@inpe.br 9 migliarno@ieav.cta.br |
| Revista | Matéria |
| Volume | 26 |
| Número | 2 |
| Páginas | e12967 |
| Histórico (UTC) | 2021-06-16 18:14:00 :: lattes -> administrator :: 2021 2022-04-03 23:14:14 :: administrator -> simone :: 2021 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | Carbon-Graphene. Composite. Recycling. Polystyrene. Microwave |
| Resumo | The electromagnetic properties of Carbon-Graphene Xerogel (CGX), Flaky graphite (GR) and Nickel-Zinc ferrite (FeNiZn) composites in polystyrene (PS) matrix were studied in the X-Band range (8.2 12.4 GHz). In this work the Expanded Polystyrene (EPS) waste material was processed into polystyrene through the recycling of EPS. The polystyrene obtained was utilized as dielectric matrix, mainly because PS is a wellknown organic polymer that presents low dielectric loss and light weight, which contribute to applications in composites for the aerospace field. In order to produce the final composite specimens, the CGX additive was previously synthesized through a sustainable method that employed the use of waste from the paper and pulp industry (black liquor). Afterwards, the morphological and structural analysis were made through Scanning Electron Microscope (SEM) and Raman Spectrometer, respectively. On the other hand, the magnetic ferrite material, FeNiZn, was obtained for the composite production through calcination, whereas the GR utilized was commercially obtained. It was observed that the increase of CGX and GR influenced on the increase of the Complex Permittivity, and that 10 wt% CGX + 50wt% FeNiZn composite sample demonstrated an absorption peak at 10.5 GHz. The results are relevant concerning the recycling of EPS waste through its use as dielectric matrix, thus developing greener and low-weight composite materials to be used in microwave applications. |
| Área | FISMAT |
| Arranjo 1 | urlib.net > BDMCI > Fonds > Produção pgr ATUAIS > CMS > Electromagnetic properties of... |
| Arranjo 2 | urlib.net > BDMCI > Fonds > Produção a partir de 2021 > CGCE > Electromagnetic properties of... |
| Arranjo 3 | urlib.net > BDMCI > Fonds > Produção a partir de 2021 > CGIP > Electromagnetic properties of... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | pt |
| Arquivo Alvo | bispo_electromagnetic.pdf |
| Grupo de Usuários | lattes |
| Grupo de Leitores | administrator lattes |
| Visibilidade | shown |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3F358GL 8JMKD3MGPCW/46KTFK8 8JMKD3MGPCW/46KUES5 |
| Lista de Itens Citando | sid.inpe.br/mtc-m21/2012/07.13.14.56.32 1 |
| Divulgação | PORTALCAPES; SCOPUS. |
| Acervo Hospedeiro | dpi.inpe.br/plutao@80/2008/08.19.15.01 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn lineage mark mirrorrepository month nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey secondarymark session shorttitle sponsor subject tertiarymark tertiarytype url |
| 7. Controle da descrição | |
| e-Mail (login) | simone |
| atualizar | |